鋁加工產(chǎn)品給人民生活帶來(lái)便利，使經(jīng)濟(jì)發(fā)展有了保障，鋁卷就是其主要代表產(chǎn)品之一，但我們?cè)谌粘Ｊ褂弥信紶栆矔?huì)遇到一些問(wèn)題，那么出現(xiàn)這些問(wèn)題的原因是什么，鋁卷生產(chǎn)廠家為你詳細(xì)解讀7點(diǎn)。
Aluminum processing products bring convenience to people's lives and guarantee economic development. Aluminum coil is one of its main representative products, but we occasionally encounter some problems in our daily use. Then what are the reasons for these problems? The aluminum coil manufacturer will read 7 points for you in detail.
1、非金屬壓痕
1. Nonmetallic indentation
定義：非金屬碎屑?jí)涸诎搴蛶У谋砻嫔?。表面呈長(zhǎng)條狀明顯點(diǎn)狀或黃黑色缺陷。主要原因是軋制工藝設(shè)備條件臟、軋制工藝潤(rùn)滑劑臟、工藝潤(rùn)滑劑注射壓力不足、板坯表面有劃痕。
Definition: Non metallic chips press on the surface of plates and strips. The surface presents long strip shaped obvious spot shaped or yellow black defects. The main reasons are that the rolling process equipment conditions are dirty, the rolling process lubricant is dirty, the injection pressure of the process lubricant is insufficient, and the slab surface has scratches.
2、滑傷
2. Slip injury
定義：由于邊緣與表面或表面與表面接觸之間的相對(duì)滑動(dòng)或錯(cuò)位而形成的劃痕
Definition: scratches caused by relative sliding or dislocation between edges and surfaces or between surfaces
主要原因：在加工和生產(chǎn)過(guò)程中，板帶與導(dǎo)軌和設(shè)備接觸時(shí)，會(huì)產(chǎn)生相對(duì)摩擦和劃痕。冷軋卷板端面未對(duì)齊，豎爐退火和翻轉(zhuǎn)造成錯(cuò)位和層間干擾。間歇性劃痕，冷軋時(shí)張力不當(dāng)，退火時(shí)層間錯(cuò)位，都會(huì)造成劃痕。不適當(dāng)?shù)恼砼鷾?zhǔn)或攤鋪操作會(huì)導(dǎo)致板間滑動(dòng)和劃痕。
Main reason: In the process of processing and production, when the strip contacts with the guide rail and equipment, it will produce relative friction and scratches. The end faces of cold rolled coils are not aligned, and shaft furnace annealing and overturning cause dislocation and interlayer interference. Intermittent scratches, improper tension during cold rolling and dislocation between layers during annealing will all cause scratches. Improper finishing approval or paving operations can cause slippage and scratches between plates.
3、碰傷
3. Bruise
定義：鋁卷或鋁卷與另一物體碰撞后，板或帶的表面或端面被劃傷，大部分金屬?gòu)陌疾圻吘壨怀觥?br /> Definition: After the aluminum coil or aluminum coil collides with another object, the surface or end face of the plate or strip is scratched, and most of the metal protrudes from the edge of the groove.
主要原因：搬運(yùn)或在存放過(guò)程中，板材或線(xiàn)圈與其他物體發(fā)生碰撞，板材或線(xiàn)圈與退火架或底盤(pán)中的其他物體發(fā)生碰撞。
Main reasons: during handling or storage, plates or coils collide with other objects, and plates or coils collide with other objects in the annealing rack or chassis.
4、翹角
4. Warping angle
定義：帶鋼邊緣在軋制或剪切后被抬起。
Definition: The edge of strip steel is lifted after rolling or shearing.
主要原因：軋制時(shí)壓下量過(guò)大，軋制時(shí)潤(rùn)滑劑分布不均，剪切時(shí)刃口調(diào)整不當(dāng)。
Main reasons: excessive reduction during rolling, uneven distribution of lubricant during rolling, improper adjustment of cutting edge during shearing.

5、折傷
5. Kink wound
定義：彎曲板材后產(chǎn)生的變形折疊。主要原因：多輥矯直機(jī)送料不正，薄板受到翻轉(zhuǎn)折疊。堆疊紙張時(shí)受力不平衡。
Definition: deformation folding after bending sheet. Main reasons: the feeding of the multi roll straightener is not correct, and the sheet is overturned and folded. The force is unbalanced when stacking paper.
6、塌卷
6. Collapse roll
定義：卷芯嚴(yán)重變形，卷形不圓。主要原因：張力不足，外壓，鐵芯強(qiáng)度低，壓接過(guò)程中無(wú)鐵芯線(xiàn)圈退火產(chǎn)生。
Definition: The winding core is seriously deformed and the winding shape is not round. Main reasons: insufficient tension, external pressure, low iron core strength, no iron core coil annealing during crimping.
7分層
7 Tiering
定義：由于層與端面層之間的不規(guī)則運(yùn)動(dòng)而導(dǎo)致帶鋼端面不平整。主要原因有鋼坯不均勻、軋機(jī)放卷和卷取張力控制不當(dāng)、壓下量和套筒移動(dòng)不均勻、校平輥調(diào)整不當(dāng)、卷取過(guò)程中對(duì)中系統(tǒng)異常、輥系平整度差等。
Definition: The end surface of strip steel is uneven due to the irregular movement between layers and end layers. The main reasons are uneven billet, improper tension control of rolling mill unwinding and coiling, uneven reduction and sleeve movement, improper adjustment of leveling roll, abnormal centering system during coiling, poor flatness of roll system, etc.
以上是鋁卷出現(xiàn)的常見(jiàn)的質(zhì)量問(wèn)題解析，提醒用戶(hù)在購(gòu)買(mǎi)時(shí)應(yīng)觀察鋁卷是否出現(xiàn)上述問(wèn)題，如果發(fā)現(xiàn)請(qǐng)立即聯(lián)系相關(guān)人員更換。關(guān)注我們http://www.rtttr1.com，了解更多相關(guān)事項(xiàng)！
The above is an analysis of the common quality problems of aluminum coils, reminding the user to observe whether the aluminum coils have the above problems when purchasing. If found, please contact the relevant personnel to replace them immediately. Follow us http://www.rtttr1.com , learn more about it!